ethylene copolymer的例句大全

Various factors affecting the slow-crack-growth ( SCG) resistance of ethylene copolymer ( denoted as polyethylene below) pipes were investigated, including the content, type, and their distribution on the backbone of the comonomers, as well as the molar mass of polyethylene.

研究了共聚单体的种类、含量以及相对分子质量、共聚单体支化链在主链上的分布等因素对聚乙烯管材料抵抗慢速裂纹扩展（SCG）性能的影响。

Results indicate that the addition of right amount of PBT with low viscosity, ethylene copolymer A, rosin ester A and rosin ester B could improve the flowability of the composites to some extent without loss of their good mechanical properties and flame retardancy.

结果表明，适量加入低粘度PBT、乙烯共聚物A、松香酯A、松香酯B可使体系在保持综合性能较好的前提下，流动性能得到不同程度的改善。

A kind of vinyl acetate ethylene copolymer emulsion was prepared. With a viscosity range from 3 300 to 4 500 mPa · s.

介绍了一种粘度在3300～4500mPa·s之间的醋酸乙烯-乙烯（VAE）共聚乳液的工艺制备方法。

Production and Market Prospect of Vinyl Acetate-ethylene Copolymer Emulsion

醋酸乙烯-乙烯共聚乳液的生产及市场前景

The toughening effects of ethylene copolymer elastomer on polypropylene ( PP)/ linear low density polyethylene ( LLDPE) blends were studied.

研究了乙烯共聚物弹性体对聚丙烯/线型低密度聚乙烯（PP/LLDPE）共混物的增韧作用。

This product adopts high molecular weight ethylene copolymer resin and goes through advanced technological flow for manufacture.

本产品采用高分子量的乙烯共聚树脂，经过先进的工艺流程制成。

Toughening Effect of Ethylene Copolymer Elastomer on PP/ LLDPE Blend

乙烯共聚物弹性体在PP/LLDPE共混物中的增韧作用

Polyethylene ( PE ) have been modified by various contents of ethylene-acrylic acid copolymer ( EAA ).

通过添加不同含量的乙烯 - 丙烯酸共聚物 ( EAA ) 改善了聚乙烯 ( PE ) 的电气性能.

As a kind of novel modifier, its toughening ability is better than that of ethylene propylene diene monomer ( EPDM) or ethylene propylene copolymer ( EPM), whether in homopolymer polypropylene, copolymer polypropylene or high fluidity polypropylene.

无论是均聚、共聚还是高流动性聚丙烯，POE的增韧效果都优于三元乙丙橡胶（EPDM）或乙丙橡胶（EPM）。

Accelerated carbonation curing of 5% ethylene/ vinyl acetate copolymer modified low heat Portland cement paste

5%乙烯-醋酸乙烯共聚物复合低热水泥浆体的碳化促进养护

Hotmelts is a major component of EVA ( ethylene vinyl acetate copolymer ).

热熔胶的主要成分是EVA ( 乙烯醋酸乙烯共聚物 ).

The graft copolymer of ethylene propylene diene monomer ( EPDM) and methyl methacrylate ( MMA) was prepared by swelling mechanochemical copolymerization in mixer.

采用直接溶胀法，在叶片混合器中以不同条件制备了三元乙丙橡胶-甲基丙烯酸甲酯接枝共聚物。

Different mechanisms to inhibit water treeing were found for ethylene-acrylic acid ( EAA ) copolymer and sorbital.

乙烯 - 丙烯酸共聚物 ( EAA ) 和三梨糖醇在抑制聚乙烯的水树形成机理上有所不同.

In the presence of organic peroxide, ethylene-vinyl acetate copolymer is graft polymerized with maleic anhydride.

通过正交实验,研究了在有机过氧化物的存在下, 乙烯 - 醋酸乙烯酯与马来酸酐接枝共聚.

This paper modified silane crosslinked polyethylene ( PE ) insulant for power cable with ethylene-vinyl acetate copolymer ( EVA ) .

采用两步法制备了硅烷 交联聚乙烯 ( PE ) 电力电缆绝缘料.

Introduced the polymerization craft , performance and application of ethylene-vinyl acetate ( EVM ) copolymer.

介绍了乙烯 — 乙酸乙烯酯 ( EVM ) 共聚合物的聚合工艺 、 性能及应用.

Effects of extender oil on the structure and properties of styrene-[ ethylene-( ethylene-propylene)]-styrene block copolymer

填充油对聚苯乙烯-b-聚〔乙烯-（乙烯-丙烯）〕-b-聚苯乙烯结构与性能的影响